1、氧化银法。用氧化银与氧化亚铜接触，封闭氯化亚铜的暴露面，达到控制腐蚀铜雕佛像的目的。先用机械方法，剔除粉状锈，露出灰白色蜡状物氯化亚铜。然后将氧化银与酒精调成糊剂，涂在氯化亚铜表面，并置于潮湿环境中，使其充分作用，形成氧化亚铜和氯化铜，覆盖氯化亚铜表面。两者皆为稳定性盐，如此多次操作，直至将器物置于高湿环境中仍不出现粉状锈的腐蚀点为止。此法适于斑点状局部腐蚀的器物及有金属镶嵌物的器物。

1, the silver oxide method. With silver oxide contact with cuprous oxide, closed the exposed surface of cuprous chloride, achieve the goal of tripod for corrosion control of Buddha. With mechanical method, first remove the powdery rust, show hoar wax cuprous chloride. Then dispatch silver oxide and alcohol into a paste, coating on the surface of cuprous chloride, and put in damp environment, make its full role, formation of cuprous oxide and cupric chloride, covering the surface of cuprous chloride. Both for the stability of salt, so operation for many times, still don't appear until put objects in high humidity environment powdery rust corrosion. This method is suitable for the mottled the implements of the local corrosion and metal tessera artifacts.

2、苯骈三氮唑法。苯骈三氮唑是杂环化合物，与铜及其盐类能形成稳定络合物，在铜合金表面生成不溶性且相当牢固的透明保护膜，使铜雕病被抑制并稳定下来，防止水蒸气和空气污染物的侵蚀。用蒸馏水和甲苯、丙酮等有机溶剂，清除铜雕佛像表面泥土油污，然后浸入苯骈三氮唑酒精溶剂中进行渗透，即可形成络合物保护膜。但苯骈三氮唑易受热升华，失去保护作用，所以最后应在铜雕表面涂一层高分子材料，做封护膜。

2, three azole nitrogen truxene method. Three azole nitrogen heterocyclic compound, truxene with copper and its salts can form stable complex compound, generate insoluble in copper alloy surface and fairly strong transparent protective film, tripod for disease suppression and stabilize, and prevent the erosion of water vapor and air pollutants. With distilled water and organic solvents such as toluene, acetone, bronze series of Buddha surface soil pollution, and then into three azole nitrogen truxene alcohol solvent penetration, can form a complex compound protective film. But three azole nitrogen is heated sublimation truxene, loss of protection, so finally should tripod for surface with a high molecular materials, sealing coating.

3、碱液浸泡法。将被腐蚀的铜雕佛像置于倍半碳酸钠溶液中浸泡，使铜的氯化物逐渐转换为稳定的铜的碳酸盐，铜雕的氯离子被置换出来转入浸液中。浸液需定时更换，直至浸液中无氯离子出现为止。随后将器物用蒸馏水反复清洗，除去碱液，干燥后封护。碱溶液仅把氯化物提取出来，保留着色彩斑斓的孔雀石等腐蚀层，不损害铜雕的原貌。此法缺点是置换反应时间长；另外氯化物不仅附在锈层表面，而且已渗入器物腐蚀结壳的深部，难以置换彻底。

3, lye soaking method. Will corrode archways of figure of Buddha in half when soaking in sodium carbonate solution, copper chloride gradually transformed into stable copper carbonate, bronze series of chloride ion replacement out into immersion. Immersion to change regularly, until no chlorine ion in immersion. Then implements repeatedly with distilled water to clean, remove the lye, sealing guard after drying. Only to chloride extraction, alkali solution retains the colorful malachite corrosion layer, such as does not harm the tripod. This defect is displacement reaction time is long; Other chloride attached to the surface of rust layer, not only in products and implements corrosion crust deep, difficult to replace thoroughly.